TUSPIPE pipes fully comply with EN 10219 S355K2H standards. Our S355K2H steel pipes offer excellent impact resistance and a higher safety margin, making them the preferred material for harsh engineering environments.
S355K2H
S355K2H structural steel pipes are often used in structural and civil engineering, as well as in the construction sector. It is a low alloy high strength steel with good shape and impact toughness that is primarily used in the manufacture of bridges, ships, vehicles, boilers, high-pressure vessels, oil and gas pipelines, power station equipment, lifting transport institutions, large steel structures, and other similar items. Use it to replace regular carbon steel, considerably reducing the weight of the construction, and ensuring the use of dependable, long-lasting materials.
Numerous designations are assigned in accordance with EN 10210. For instance,
- The symbol K in combination with either numerical i.e. 0 or 2, would mean that the specific impact properties of EN 10219 S355K2H Steel Pipeat specific temperature points of 0℃ and – 40℃ apiece.
- The letter H is a designation intended for hollow sectioned products like the S355K2H Pipe.
- The other designation that touches the base with regards to its application is the letter S, which is a typical feature of structural steel.
Pourquoi choisir tuspipe ?
Depuis 1998, Tianjin United Steel Piping Co., Ltd (TUSPIPE) s'engage à fournir des tubes de canalisation de haute qualité.
Avec une capacité de production annuelle de plus de 500 000 tonnes, l'entreprise dessert divers domaines et industries, tels que l'exploitation et la transmission du pétrole et du gaz, la construction navale et automobile, l'eau et l'électricité, la protection de l'environnement, l'ingénierie mécanique, la construction d'infrastructures, etc.
TUSPIPE accorde une grande importance à la qualité des produits et à leur contrôle rigoureux. Afin de maintenir une bonne qualité des produits, l'entreprise a mis en place un centre d'essai et d'inspection depuis 2004. Doté d'une série d'équipements d'essai et d'inspection de pointe, le centre d'essai et d'inspection est en mesure d'effectuer des essais de traction, des essais hydrauliques, des essais d'impact, des essais DWTT, etc.
Designation for EN 10219 S355K2H Steel Grade
- Le nombre de ces Norme européenne (spécification EN 10219) ;
- La lettre majuscule S pour l'acier de construction ;
- L'indication de la limite d'élasticité minimale spécifiée pour une épaisseur ≤16mm est exprimée en N/mm2 ;
- Les lettres majuscules JR désignent les qualités dont les propriétés d'impact à température ambiante sont spécifiées ;
- La lettre majuscule J et un nombre 0 ou 2 pour les qualités ayant des propriétés d'impact spécifiées à 0℃ et -20℃ respectivement ;
- La lettre majuscule H indique les sections creuses
Dimensions and Sizes of EN10219 S355K2H Pipe
| DN | O. D. | W. T. | |||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Pouce | mm | SCH5S | SCH10S | SCH10 | SCH20 | SCH30 | SCH40 | SCH60 | SCH80 | SCH100 | SCH120 | SCH140 | SCH160 | Sth | XS | XXS | |
| 50 | 2″ | 60.3 | 1.65 | 2.77 | - | - | - | 3.91 | - | 5.54 | - | - | - | 8.74 | 3.91 | 5.54 | 11.07 |
| 65 | 2 1/2″ | 73 | 2.11 | 3.05 | - | - | - | 5.16 | - | 7.01 | - | - | - | 9.53 | 5.16 | 7.01 | 14.02 |
| 80 | 3″ | 88.9 | 2.11 | 3.05 | - | - | - | 5.49 | - | 7.62 | - | - | - | 11.13 | 5.49 | 7.52 | 15.24 |
| 90 | 3 1/2″ | 101.6 | 2.11 | 3.05 | - | - | - | 5.74 | - | 8.08 | - | - | - | - | 5.74 | 8.08 | - |
| 100 | 4″ | 114.3 | 2.11 | 3.05 | - | - | - | 6.02 | - | 8.58 | - | 11.13 | - | 13.49 | 6.02 | 8.56 | 17.12 |
| 125 | 5″ | 141.3 | 2.77 | 3.4 | - | - | - | 6.55 | - | 9.53 | - | 12.7 | - | 15.88 | 6.55 | 9.53 | 18.05 |
| 150 | 6″ | 168.3 | 2.77 | 3.4 | - | - | - | 7.11 | - | 10.97 | - | 14.27 | - | 18.26 | 7.11 | 10.97 | 21.95 |
| 200 | 8″ | 219.1 | 2.77 | 3.76 | - | 6.35 | 7.04 | 8.18 | 10.31 | 12.7 | 15.09 | 18.26 | 20.62 | 23.01 | 8.18 | 12.7 | 22.23 |
| 250 | 10″ | 273.1 | 3.4 | 4.19 | - | 6.35 | 7.8 | 9.27 | 12.7 | 15.09 | 18.26 | 21.44 | 25.4 | 28.58 | 9.27 | 12.7 | 25.4 |
| 300 | 12″ | 323.9 | 3.96 | 4.57 | - | 6.35 | 8.38 | 10.31 | 14.27 | 17.48 | 21.44 | 25.4 | 28.58 | 33.32 | 9.53 | 12.7 | 25.4 |
| 350 | 14″ | 355.5 | 3.96 | 4.78 | 6.35 | 7.92 | 9.53 | 11.13 | 15.09 | 19.05 | 23.83 | 27.79 | 31.75 | 35.71 | 9.53 | 12.7 | - |
| 400 | 16″ | 406.4 | 4.19 | 4.78 | 6.35 | 7.92 | 9.53 | 12.7 | 16.66 | 21.44 | 26.19 | 30.96 | 36.53 | 40.49 | 9.53 | 12.7 | - |
| 450 | 18″ | 457.2 | 4.19 | 4.78 | 6.35 | 7.92 | 11.13 | 14.27 | 19.05 | 23.83 | 39.36 | 34.93 | 39.67 | 45.24 | - | - | - |
| 500 | 20″ | 508 | 4.78 | 5.54 | 6.35 | 9.53 | 12.7 | 15.09 | 20.62 | 26.19 | 32.54 | 38.1 | 44.45 | 50.01 | - | - | - |
| 550 | 22″ | 558.8 | 4.78 | 5.54 | 6.35 | 9.53 | 12.7 | - | 22.23 | 28.58 | 34.93 | 41.28 | 47.63 | 53.98 | - | - | - |
| 600 | 24″ | 609.6 | 5.54 | 6.35 | 6.35 | 9.53 | 14.27 | 17.48 | 24.61 | 30.96 | 38.89 | 46.02 | 52.37 | 59.54 | - | - | - |
Weldability of EN 10219 S355K2H Pipe
Cette norme européenne n'autorise que l'utilisation d'acier soudable. Les normes EN 1011-1 et EN 1011-2 spécifient les paramètres critiques pour le soudage des produits couverts par cette norme européenne.
Lors du soudage de ces matériaux, la principale préoccupation est l'apparition de fissures à froid dans la zone soudée, au fur et à mesure que l'épaisseur, le niveau de résistance et le CEV du produit augmentent. La fissuration à froid se produit pour diverses raisons :
- Augmentation des concentrations d'hydrogène diffusible dans le métal soudé ;
- Structure fragile dans la zone affectée thermiquement ;
- Concentrations élevées de contraintes de traction dans le joint soudé
Chemical Composition % of Steel S355K2H (1.0576): EN 10219
| Désignation | Type de désoxydation | Sub Grop | C % max. Épaisseur nominale (mm) | Si % max. | Mn % max. | P % max. | S % max. | N % max. | |
|---|---|---|---|---|---|---|---|---|---|
| According to EN10219 | ≤40 | ＞40≤65 | |||||||
| S355K2H | FF | QS | 0.22 | 0.22 | 0.55 | 1.6 | 0.03 | 0.03 | - |
| 1) The deoxidation methods are designated as follows: FF-Full killed steel containing nitrogen binding elements in amounts sufficient to bind available nitrogen (e.g.min.0.020% total Al, or 0.015% soluble Al). 2) QS-quality steel. 3) It is permissible to exceed the specified values provided that for each increase of 0.001%N the P max content will be reduced by 0.005%, the N content of the ladle analysis, however, shall not be more than 0.012% 4) The max. value for nitrogen does not apply if the chemical composition shows a minimum total Al content of0.020% with a minimum AL/N ratio of 2:1, or if sufficient other N-binding elements are present. The N-binding elements shall be recorded in Inspection Document. | |||||||||
Mechanical Properties for S355K2H Non-alloy Structural Steel
| Qualité de l'acier | Propriétés mécaniques | Impact Energy (KV J) | ||||
|---|---|---|---|---|---|---|
| Limite d'élasticité | Résistance à la traction | Élongation | Test Temperature At Test Temperature of ℃ | |||
| (Mpa) | (Mpa) | (%) | -20 | 0 | 20 | |
| S355K2H | 355 | 510-680 | 22 | 40 | - | - |
Manufacturing Tolerances of EN 10219 S355K2H Pipe
| Caractéristique | Sections creuses rondes | Sections creuses carrées et rectangulaires |
|---|---|---|
| Dimension extérieure | ± 1% avec min ± 0,5mm et max ± 10mm | ± 1% avec un minimum de ± 0,5mm |
| Épaisseur (T) | T≤5mm : ±10% | T≤5mm : ±10% |
| T>5mm : ± 0,5mm | T>5mm : ± 0,5mm | |
| L'absence d'arrondi | 2% | - |
| Convexité | - | Max .8% avec min 0.5mm |
| Équilibre des côtés | - | 90° ± 1° |
| Profilé d'angle extérieur | - | T≤6mm : 1,6T à 2,4T |
| - | 6<T≤10mm : 2.0T à 3.0T | |
| - | T,10 : 2.4T à 3.6T | |
| Torsion | - | 2mm plus 0,5mm/m |
| Rectitude | 0,2% du total | 0,15% du total |
| Masse | ±6% sur la longueur individuelle | |
Inspection and Testing of EN 10219 S355K2H Hollow Sections
EN 10219 S355K2H is tensile tested according to EN 10002-1 and Charpy impact tested according to EN 10045-1.
| Inspection or test type | Test frequency | ||
|---|---|---|---|
| Internal tests | Acceptance test | ||
| Mandatory | Chemical analysis | M | M |
| Tensile testing | M | One per tested batch | |
| Dimension verification | M | M | |
| Visual inspection | M | M | |
| Optional | Flattening test or expansion test (option 18) | M | One per tested batch |
| Roughness testing | Non applicable | One per tested batch | |
| NDT of the weld in order to identify any longitudinal discontinuities | Non applicable | Individual | |
| NDT in order to detect any leaks | |||
Marking of EN10219 S355K2H
Except as provided for in EN10219 10.2 for hollow sections which are bundled, each S355J0H section shall be marked by suitable and durable methods such as painting, stamping, adhesive labels, or attached tags with the following:
— the steel designation e.g., EN 10219-S355JOH;
— the manufacturer’s name or trademark;
— in the case of specific inspection: an identification number, e.g., order number, which permits the correlation of the product or delivery unit to the related document;
— the mark of the external inspection representative (where applicable).
When the items are provided bundled, the EN10219 10.1 marking must be on a label that is firmly affixed to the bundle.