S235JRH
TUSPIPE manufactures its products strictly in accordance with EN 10219 S235JRH standards. Our S235JRH type steel pipes are structurally stable and reliable, making them an ideal choice for a variety of engineering applications.
S235JRH
The EN 10219 S235JRH pipe is made in accordance with all applicable ASTM, ASME, and international standards. These pipes have greater corrosion resistance and are suitable for use in a variety of temperatures.
Cold-Formed S235JRH Steel Welded Pipe has tensile strengths ranging from 316Mpa to 510Mpa and yield strength of at least 235Mpa. These pipes may be readily extended by 26%. The S235JRH Tube is widely utilized in civil engineering applications such as bridge construction, structural frames, factory structures, and mechanical engineering systems.
タスパイプを選ぶ理由
1998年以来、天津聯合鋼管有限公司(TUSPIPE)は高品質のラインパイプの供給に尽力しています。
年間生産能力は50万トンを超え、石油・ガス開発、送電、船舶・自動車建造、水・電気、環境保護、機械工学、インフラ建設など、さまざまな分野・業界にサービスを提供している。
TUSPIPEは製品の品質を重視し、厳格な品質管理を行っている。製品の品質を維持するため、2004年から試験検査センターを設立しました。最新の試験・検査設備を備え、引張試験、水力試験、衝撃試験、DWTTなどを実施することができます。
Designation for EN 10219 S235JRH Steel Grade
- この数は 欧州規格 (EN 10219仕様）；
- 構造用鋼を表す大文字のS；
- 厚さ≦16mm の場合の最低降伏強度の表示は、N/mm2 で表す；
- 大文字のJRは、室温での衝撃特性が規定されている品質を表す；
- 大文字のJと数字の0または2は、それぞれ0℃と-20℃で指定された衝撃特性を持つ品質を表す；
- 大文字のHは中空部分を示す
Dimensions and Sizes of EN10219 S235JRH Pipe
| 識別名 | O.D. | W.T. | |||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| インチ | mm | SCH5S | SCH10S | SCH10 | SCH20 | SCH30 | SCH40 | SCH60 | SCH80 | SCH100 | SCH120 | SCH140 | SCH160 | ス | XS | XXS | |
| 50 | 2″ | 60.3 | 1.65 | 2.77 | - | - | - | 3.91 | - | 5.54 | - | - | - | 8.74 | 3.91 | 5.54 | 11.07 |
| 65 | 2 1/2″ | 73 | 2.11 | 3.05 | - | - | - | 5.16 | - | 7.01 | - | - | - | 9.53 | 5.16 | 7.01 | 14.02 |
| 80 | 3″ | 88.9 | 2.11 | 3.05 | - | - | - | 5.49 | - | 7.62 | - | - | - | 11.13 | 5.49 | 7.52 | 15.24 |
| 90 | 3 1/2″ | 101.6 | 2.11 | 3.05 | - | - | - | 5.74 | - | 8.08 | - | - | - | - | 5.74 | 8.08 | - |
| 100 | 4″ | 114.3 | 2.11 | 3.05 | - | - | - | 6.02 | - | 8.58 | - | 11.13 | - | 13.49 | 6.02 | 8.56 | 17.12 |
| 125 | 5″ | 141.3 | 2.77 | 3.4 | - | - | - | 6.55 | - | 9.53 | - | 12.7 | - | 15.88 | 6.55 | 9.53 | 18.05 |
| 150 | 6″ | 168.3 | 2.77 | 3.4 | - | - | - | 7.11 | - | 10.97 | - | 14.27 | - | 18.26 | 7.11 | 10.97 | 21.95 |
| 200 | 8″ | 219.1 | 2.77 | 3.76 | - | 6.35 | 7.04 | 8.18 | 10.31 | 12.7 | 15.09 | 18.26 | 20.62 | 23.01 | 8.18 | 12.7 | 22.23 |
| 250 | 10″ | 273.1 | 3.4 | 4.19 | - | 6.35 | 7.8 | 9.27 | 12.7 | 15.09 | 18.26 | 21.44 | 25.4 | 28.58 | 9.27 | 12.7 | 25.4 |
| 300 | 12″ | 323.9 | 3.96 | 4.57 | - | 6.35 | 8.38 | 10.31 | 14.27 | 17.48 | 21.44 | 25.4 | 28.58 | 33.32 | 9.53 | 12.7 | 25.4 |
| 350 | 14″ | 355.5 | 3.96 | 4.78 | 6.35 | 7.92 | 9.53 | 11.13 | 15.09 | 19.05 | 23.83 | 27.79 | 31.75 | 35.71 | 9.53 | 12.7 | - |
| 400 | 16″ | 406.4 | 4.19 | 4.78 | 6.35 | 7.92 | 9.53 | 12.7 | 16.66 | 21.44 | 26.19 | 30.96 | 36.53 | 40.49 | 9.53 | 12.7 | - |
| 450 | 18″ | 457.2 | 4.19 | 4.78 | 6.35 | 7.92 | 11.13 | 14.27 | 19.05 | 23.83 | 39.36 | 34.93 | 39.67 | 45.24 | - | - | - |
| 500 | 20″ | 508 | 4.78 | 5.54 | 6.35 | 9.53 | 12.7 | 15.09 | 20.62 | 26.19 | 32.54 | 38.1 | 44.45 | 50.01 | - | - | - |
| 550 | 22″ | 558.8 | 4.78 | 5.54 | 6.35 | 9.53 | 12.7 | - | 22.23 | 28.58 | 34.93 | 41.28 | 47.63 | 53.98 | - | - | - |
| 600 | 24″ | 609.6 | 5.54 | 6.35 | 6.35 | 9.53 | 14.27 | 17.48 | 24.61 | 30.96 | 38.89 | 46.02 | 52.37 | 59.54 | - | - | - |
Weldability of EN 10219 S235JRH Pipe
This European standard specifies weldable steel. EN 1011-1 and EN 1011-2 provide the essential specifications for welding items covered by this European standard.
The greatest concern while welding these materials is the development of cold cracking in the welded zone as the thickness, strength level, and CEV of the product increase. Cold cracking occurs as a result of the following factors:
- 溶接金属中の拡散性水素濃度の上昇；
- 熱影響部の脆性構造；
- 溶接継手の高い引張応力集中
Chemical composition of S235JRH for product thicknesses ≤ 40 mm (Heat analysis in %)
| 鋼種 | Material Number | Type of Deoxidation1) | C | Si | ムン | P | S | N2) |
|---|---|---|---|---|---|---|---|---|
| S235JRH | 1.0039 | FF | ≤ 0,17 | - | ≤ 1,40 | ≤ 0,040 | ≤ 0,040 | ≤ 0,009 |
| FF = Fully killed steel containing nitrogen binding elements in amounts sufficient to bind available nitrogen (e. g. min. 0,020 % total Al or 0,015 % soluble Al). | ||||||||
| The maximum value for nitrogen does not apply if the chemical composition shows a minimum total Al content of 0,020 % with a minimum Al/N ratio of 2:1, or if sufficient other N-binding elements are present. The N-binding elements shall be recorded in the Inspection Document. | ||||||||
Mechanical Properties of S235JRH at Room Temperature
| 鋼種 | Material Number | Yield Strength ReH N/mm² min. for Nominal Wall Thickness in mm | 引張強度 Rm N/mm² for Nominal Wall Thickness in mm | Elongation A 4) % 分。 for Nominal Wall Thickness in mm | Impact Energy KV5) J 分。 at a Temperature °C of | ||||
|---|---|---|---|---|---|---|---|---|---|
| £ 16 | > 16 £ 40 | < 3 | ≥ 3 ≤40 | ≤40 | -20 | 0 | 20 | ||
| S235JRH1) | 1.0039 | 235 | 225 | 360 -510 | 360 – 510 | 242) | - | - | 27 |
| The impact test has to be proved only if option 1.3 is determined. For wall thicknesses > 3 mm and section sizes D/T < 15 (circular) and (B+H)/2T x 12,5 (square or rectangular) the minimum elongation is reduced by 2. For wall thicknesses £ 3 mm the minimum value for elongation is 17 %. For section sizes D/T < 15 (circular) and (B+H)/2T x 12,5 (square or rectangular) the minimum elongations are reduces by 2. For wall thickness below 3 mm see DIN EN 10219-1, 9.2.2. For impact tests with test pieces with reduced cross-section see DIN EN 10219-1, 6.7.2. | |||||||||
Manufacturing Tolerances of EN 10219 S235JRH Pipe
| 特徴 | 丸型中空断面 | 正方形および長方形中空断面 |
|---|---|---|
| 外寸 | 最小±0.5mm、最大±10mmの±1% | ± 1% 最小±0.5mm |
| 厚さ (T) | T≤5mm: ±10% | T≤5mm: ±10% |
| T>5mm: ± 0.5mm | T>5mm: ± 0.5mm | |
| アウト・オブ・ラウンド | 2% | - |
| 凸 | - | 最小0.5mmの最大.8% |
| 側面の直角度 | - | 90° ± 1° |
| エクスターナル・コーナー・プロファイル | - | T≦6mm：1.6T〜2.4T |
| - | 6<T≤10mm：2.0T〜3.0T | |
| - | T,10：2.4Tから3.6T | |
| ツイスト | - | 2mmプラス0.5mm/m |
| 真直度 | 全体の0.2% | 全体の0.15% |
| 質量 | 個々の長さについて±6% | |
Inspection and Testing of EN 10219 S235JRH Hollow Sections of Non-alloy Steels
EN 10219 S235JRH is tensile tested according to EN 10002-1 and Charpy impact tested according to EN 10045-1.
| 検査要件 | 検査頻度 | |||
|---|---|---|---|---|
| テストの種類 | 非特定 検査 | 特定検査 | ||
| 必須 テスト | 1 | キャスト分析 | 1配送につき1件 項目 | キャスト1人につき1枚 |
| 2 | 引張試験 | 1配送につき1件 項目 | テスト・ユニット1台につき1個（b） | |
| 3 | 衝撃試験 品質J2およびK2のみ | 該当なし | テストユニット1台につき1セット (b) | |
| 4 | 表面状態 寸法 | - | - | |
| 5 | 溶接部のNDT | 該当なし | 全製品、フルレングス | |
| オプション テスト | 6 | 製品分析 | 該当なし | テストユニット1台につき1つ |
| 7 | キャスト分析 追加要素 | 該当なし | オプション1.2を参照 | |
| 8 | 衝撃試験 品質JRとJ0 | 該当なし | テストユニット1台につき1セット (b) | |
| b - 縦方向または横方向のサンプルは、メーカーの判断による。 | ||||