S355J2H
TUSPIPE not only manufactures high-strength structural steel pipes according to the EN 10219 S355J2H standard, but also achieves superior quality at every stage of manufacturing. Our S355J2H products possess excellent load-bearing capacity and stability.
S355J2H
Grade S355J2H is a low-carbon manganese-containing steel alloy. This medium tensile carbon steel possesses both good weldable properties as well as good impact resistance. Steel grade S355J2h is also well suited to be employed in sub-zero temperature applications. There are several designations allocated under specification EN 10210. For instance, the symbol J in combination with either numerical i.e. 0 or 2, would mean that the specific impact properties of EN 10219 S355J2H Steel Pipe at specific temperature points of 0℃ and – 20℃ apiece.
The letter H is a designation intended for hollow sectioned products like the S355J2H Pipe. The other designation that touches the base with regards to its application is the letter S, which is a typical feature of structural steel. There are several reasons as to why the EN 10219 S355J2H Seamless Pipe exhibits good impact strength. Firstly, the chemistry of the carbon steel group contains manganese, which not only improves its strength but also improves the hardness properties of the S355J2H EN 10219 Pipes. Secondly, in comparison to regular pipes, hollow sections have thicker walls. A thicker cross-section also makes EN 10219 Grade S355J2H Hot Finished CHS sturdy and very durable.
タスパイプを選ぶ理由
1998年以来、天津聯合鋼管有限公司(TUSPIPE)は高品質のラインパイプの供給に尽力しています。
年間生産能力は50万トンを超え、石油・ガス開発、送電、船舶・自動車建造、水・電気、環境保護、機械工学、インフラ建設など、さまざまな分野・業界にサービスを提供している。
TUSPIPEは製品の品質を重視し、厳格な品質管理を行っている。製品の品質を維持するため、2004年から試験検査センターを設立しました。最新の試験・検査設備を備え、引張試験、水力試験、衝撃試験、DWTTなどを実施することができます。
Designation for EN 10219 S355J2H Steel Grade
- この数は 欧州規格 (EN 10219仕様）；
- 構造用鋼を表す大文字のS；
- 厚さ≦16mm の場合の最低降伏強度の表示は、N/mm2 で表す；
- 大文字のJRは、室温での衝撃特性が規定されている品質を表す；
- 大文字のJと数字の0または2は、それぞれ0℃と-20℃で指定された衝撃特性を持つ品質を表す；
- 大文字のHは中空部分を示す
Dimensions and Sizes of EN10219 S355J2H Pipe
| 識別名 | O.D. | W.T. | |||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| インチ | mm | SCH5S | SCH10S | SCH10 | SCH20 | SCH30 | SCH40 | SCH60 | SCH80 | SCH100 | SCH120 | SCH140 | SCH160 | ス | XS | XXS | |
| 50 | 2″ | 60.3 | 1.65 | 2.77 | - | - | - | 3.91 | - | 5.54 | - | - | - | 8.74 | 3.91 | 5.54 | 11.07 |
| 65 | 2 1/2″ | 73 | 2.11 | 3.05 | - | - | - | 5.16 | - | 7.01 | - | - | - | 9.53 | 5.16 | 7.01 | 14.02 |
| 80 | 3″ | 88.9 | 2.11 | 3.05 | - | - | - | 5.49 | - | 7.62 | - | - | - | 11.13 | 5.49 | 7.52 | 15.24 |
| 90 | 3 1/2″ | 101.6 | 2.11 | 3.05 | - | - | - | 5.74 | - | 8.08 | - | - | - | - | 5.74 | 8.08 | - |
| 100 | 4″ | 114.3 | 2.11 | 3.05 | - | - | - | 6.02 | - | 8.58 | - | 11.13 | - | 13.49 | 6.02 | 8.56 | 17.12 |
| 125 | 5″ | 141.3 | 2.77 | 3.4 | - | - | - | 6.55 | - | 9.53 | - | 12.7 | - | 15.88 | 6.55 | 9.53 | 18.05 |
| 150 | 6″ | 168.3 | 2.77 | 3.4 | - | - | - | 7.11 | - | 10.97 | - | 14.27 | - | 18.26 | 7.11 | 10.97 | 21.95 |
| 200 | 8″ | 219.1 | 2.77 | 3.76 | - | 6.35 | 7.04 | 8.18 | 10.31 | 12.7 | 15.09 | 18.26 | 20.62 | 23.01 | 8.18 | 12.7 | 22.23 |
| 250 | 10″ | 273.1 | 3.4 | 4.19 | - | 6.35 | 7.8 | 9.27 | 12.7 | 15.09 | 18.26 | 21.44 | 25.4 | 28.58 | 9.27 | 12.7 | 25.4 |
| 300 | 12″ | 323.9 | 3.96 | 4.57 | - | 6.35 | 8.38 | 10.31 | 14.27 | 17.48 | 21.44 | 25.4 | 28.58 | 33.32 | 9.53 | 12.7 | 25.4 |
| 350 | 14″ | 355.5 | 3.96 | 4.78 | 6.35 | 7.92 | 9.53 | 11.13 | 15.09 | 19.05 | 23.83 | 27.79 | 31.75 | 35.71 | 9.53 | 12.7 | - |
| 400 | 16″ | 406.4 | 4.19 | 4.78 | 6.35 | 7.92 | 9.53 | 12.7 | 16.66 | 21.44 | 26.19 | 30.96 | 36.53 | 40.49 | 9.53 | 12.7 | - |
| 450 | 18″ | 457.2 | 4.19 | 4.78 | 6.35 | 7.92 | 11.13 | 14.27 | 19.05 | 23.83 | 39.36 | 34.93 | 39.67 | 45.24 | - | - | - |
| 500 | 20″ | 508 | 4.78 | 5.54 | 6.35 | 9.53 | 12.7 | 15.09 | 20.62 | 26.19 | 32.54 | 38.1 | 44.45 | 50.01 | - | - | - |
| 550 | 22″ | 558.8 | 4.78 | 5.54 | 6.35 | 9.53 | 12.7 | - | 22.23 | 28.58 | 34.93 | 41.28 | 47.63 | 53.98 | - | - | - |
| 600 | 24″ | 609.6 | 5.54 | 6.35 | 6.35 | 9.53 | 14.27 | 17.48 | 24.61 | 30.96 | 38.89 | 46.02 | 52.37 | 59.54 | - | - | - |
Weldability of EN 10219 S355J2H Pipe
この欧州規格は、溶接可能な鋼材の使用のみを認めている。EN 1011-1およびEN 1011-2は、この欧州規格の対象製品の溶接に関する重要なパラメータを規定しています。
このような材料を溶接する場合、製品の厚さ、強度レベル、CEVが大きくなるにつれて、溶接部に低温割れが発生することが最大の心配事となる。冷間割れはさまざまな理由で発生する：
- 溶接金属中の拡散性水素濃度の上昇；
- 熱影響部の脆性構造；
- 溶接継手の高い引張応力集中
Chemical Composition % of Steel S355J2H (1.0576): EN 10219
| 指定 | 脱酸の種類 | Sub Grop | C % マックスだ。 公称厚さ(mm) | Si % マックスだ。 | ムン % マックスだ。 | P % マックスだ。 | S % マックスだ。 | N % マックスだ。 | ||
|---|---|---|---|---|---|---|---|---|---|---|
| EN10219に準拠 | EN10219に準拠 | ≤40 | ＞40≤65 | |||||||
| S355J2H | 1.0576 | FF | QS | 0.22 | 0.22 | 0.55 | 1.6 | 0.03 | 0.03 | - |
- The deoxidation methods are designated as follows:
FF-Full killed steel containing nitrogen binding elements in amounts sufficient to bind available nitrogen (e.g.min.0.020% total Al, or 0.015% soluble Al).
- QS-quality steel.
- It is permissible to exceed the specified values provided that for each increase of 0.001%N the P max content will be reduced by 0.005%, the N content of the ladle analysis, however, shall not be more than 0.012%
- The max. value for nitrogen does not apply if the chemical composition shows a minimum total Al content of0.020% with a minimum AL/N ratio of 2:1, or if sufficient other N-binding elements are present. The N-binding elements shall be recorded in inspection Document.
Mechanical Properties for S355J2H Non-alloy Structural Steel
| 指定 | Minimum Yield Strength REh で N/mm2 | Tensile Strength Rm で N/mm2 | Minimum percentage elongation L0-5,65√S0 | Impact properties | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| EN10219に準拠 | EN10219に準拠 | Nominal thickness in mm | Nominal thickness in mm | 縦型 | 横断 | Test Temperature | Minimum average absorbed energy(J)for standard test pieces | |||||
| ≤16 | ＞16≤40 | ＞40≤65 | ＜3 | ≥3≤65 | Nominal thickness in mm | |||||||
| ≤40 | ＞40≤65 | ≤40 | ＞40≤65 | |||||||||
| S355J2H | 1.0576 | 355 | 345 | 335 | 510-680 | 490-630 | 22 | 21 | 20 | 19 | -20 | 27 |
Manufacturing Tolerances of EN 10219 S355J2H Pipe
| 特徴 | 丸型中空断面 | 正方形および長方形中空断面 |
|---|---|---|
| 外寸 | 最小±0.5mm、最大±10mmの±1% | ± 1% 最小±0.5mm |
| 厚さ (T) | T≤5mm: ±10% | T≤5mm: ±10% |
| T>5mm: ± 0.5mm | T>5mm: ± 0.5mm | |
| アウト・オブ・ラウンド | 2% | - |
| 凸 | - | 最小0.5mmの最大.8% |
| 側面の直角度 | - | 90° ± 1° |
| エクスターナル・コーナー・プロファイル | - | T≦6mm：1.6T〜2.4T |
| - | 6<T≤10mm：2.0T〜3.0T | |
| - | T,10：2.4Tから3.6T | |
| ツイスト | - | 2mmプラス0.5mm/m |
| 真直度 | 全体の0.2% | 全体の0.15% |
| 質量 | 個々の長さについて±6% | |
Inspection and Testing of EN 10219 S355J2H Hollow Sections of Non-alloy Steels
EN 10219 S355J2H is tensile tested according to EN 10002-1 and Charpy impact tested according to EN 10045-1.
| 検査要件 | 検査頻度 | |||
|---|---|---|---|---|
| テストの種類 | Non-specific inspection | 特定検査 | ||
| 必須 テスト | 1 | キャスト分析 | 1配送につき1件 項目 | キャスト1人につき1枚 |
| 2 | 引張試験 | 1配送につき1件 項目 | テスト・ユニット1台につき1個（b） | |
| 3 | 衝撃試験 品質J2およびK2のみ | 該当なし | テストユニット1台につき1セット (b) | |
| 4 | 表面状態 寸法 | - | - | |
| 5 | 溶接部のNDT | 該当なし | 全製品、フルレングス | |
| オプション テスト | 6 | 製品分析 | 該当なし | テストユニット1台につき1つ |
| 7 | キャスト分析 追加要素 | 該当なし | オプション1.2を参照 | |
| 8 | 衝撃試験 品質JRとJ0 | 該当なし | テストユニット1台につき1セット (b) | |
| b - 縦方向または横方向のサンプルは、メーカーの判断による。 | ||||
Marking of EN10219 S355J2H
Except as provided for in 10.2 for S355J2H hollow sections which are bundled, each hollow section shall be marked by suitable and durable methods such as painting, stamping, adhesive labels or attached tags with the following:
— the steel designation e.g., EN 10219-S355J2H;
- メーカー名または商標；
- 特定検査の場合：製品または納入単位と関連文書との関連付けを可能にする識別番号、例えば注文番号；
- 外部検査担当者のマーク（該当する場合）。
If the product is supplied in bundles, the mark required in EN10219 10.1 shall be on the label, which shall be firmly attached to the bundle product.